I-Carbon Steel Shot ephansi
Isici somkhiqizo
Ukuqina okuphezulu, ukuqina okuphezulu, impilo ende yesevisi.
Ukuqhekeka okuphansi, uthuli oluphansi, ukungcola okuphansi.
Ukuguga okuphansi kwezinto zokusebenza, impilo ende yesisekeli.
Yehlisa umthwalo wesistimu yokukhipha i-dedusting, andise isikhathi sokusetshenziswa kwezinto zokususa izinto.
Ukucaciswa kobuchwepheshe
Ukwakheka Kwekhemikhali% | C | 0.10-0.20% |
Si | 0.10-0.35% | |
Mn | 0.35-1.50% | |
S | ≤0.05% | |
P | ≤0.05% | |
Ezinye izakhi ze-alloy | Ukungeza u-Cr Mo Ni B Al Cu njll. | |
Ukuqina | HRC42-48 / 48-54 | |
I-Microstructure | Isakhiwo se-Duplex sihlanganise i-Martensite ne-Bainite | |
Ukuminyana | ≥ 7.2g/cm3 | |
Ifomu langaphandle | I-Spherical |
Ukusabalalisa usayizi
Isikrini No. | Intshi | Usayizi wesikrini | S70 | I-S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
6 | 0.132 | 3.35 | Konke kuyadlula | |||||||||||
7 | 0.111 | 2.80 | Konke kuyadlula | |||||||||||
8 | 0.0937 | 2.36 | Konke kuyadlula | ≥90% | ||||||||||
10 | 0.0787 | 2.00 | Konke kuyadlula | Konke kuyadlula | ≥85% | ≥97% | ||||||||
12 | 0.0661 | 1.70 | Konke kuyadlula | ≤5% | ≥85% | ≥97% | ||||||||
14 | 0.0555 | 1.40 | Konke kuyadlula | ≤5% | ≥85% | ≥97% | ||||||||
16 | 0.0469 | 1.18 | Konke kuyadlula | ≤5% | ≥85% | ≥97% | ||||||||
18 | 0.0394 | 1.00 | Konke kuyadlula | ≤5% | ≥85% | ≥96% | ||||||||
20 | 0.0331 | 0.850 | Konke kuyadlula | ≤10% | ≥85% | ≥96% | ||||||||
25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
30 | 0.0232 | 0.600 | Konke kuyadlula | ≥85% | ≥96% | |||||||||
35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
40 | 0.0165 | 0.425 | Konke Kudlula | ≥85% | ||||||||||
45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
50 | 0.0117 | 0.300 | ≥80% | |||||||||||
80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
120 | 0.0049 | 0.125 | ≥90% | |||||||||||
200 | 0.0029 | 0.075 |
Ukukhathala Life Test
Umdwebo Wokuqhathanisa Wokusetshenziswa we-TAAI-LCB steel shot, isibhamu sensimbi enekhabhoni ephansikanye nokudubula kwensimbi enekhabhoni ephezulu.(isivivinyo sempilo yokukhathala samabanga ajwayelekile ngokwesilinganiso sesivinini esinomthelela esingu-60.96m/s)
Ukungafani kokusetshenziswa-Ibanga elijwayelekile
Ngokuhlola impilo yokukhathala singabona ukuthi: impilo yesevisi ye-TAAI-LCB Steel Shotyinde ngokuphindwe ngo-1.5 kunokudubula okujwayelekile okuphansi kwe-carbon steel, izikhathi ezi-2 kuneshothi yensimbi ephezulu ye-carbon.
Isicelo
Ukuhlanza ukuqhuma: Kusetshenziselwa ukuhlanza ukuqhuma kokusakazwa, ukufakela, ukubumba;ukususwa kwesihlabathi kokusakazwa, ipuleti lensimbi, uhlobo lwensimbi H, isakhiwo sensimbi.
Ukususwa kokugqwala: Ukususwa kokugqwala kokusakazwa, ukubumba, ipuleti lensimbi, uhlobo lwensimbi H, isakhiwo sensimbi.
I-shot peening: Ukuvula isibhamu kwegiya, izingxenye eziphathwe ukushisa.
Ukuqhunyiswa kwesihlabathi: Ukuqhunyiswa kwesihlabathi sensimbi yephrofayili, ibhodi lomkhumbi, ibhodi lensimbi, impahla yensimbi, isakhiwo sensimbi.
Ukwelashwa kwangaphambili: Ukwelashwa kwangaphambili kwendawo, ibhodi lensimbi, insimbi yephrofayili, isakhiwo sensimbi, ngaphambi kokupenda noma ukumbozwa.